Made from pure PTFE dispersed resin through defatting, drawing, slitting and plying. White and soft. Film thickness about 0.02–0.04 mm, with uniform gram weight and high tensile strength after plying.
Inquire about PTFE Yarn| Model | Size (g/m) | Density (g/m³) | PTFE content (%) | tensile breaking strength (N) | elongation at break (%) |
|---|---|---|---|---|---|
| 4103-2 | 2.0±0.2 | 1.2±0.2 | 100 | ＞ 60 | ≤ 30 |
| 4103-3 | 3.0±0.2 | 1.2±0.2 | 100 | ＞ 70 | ≤ 30 |
| 4103-5 | 5.0±0.2 | 1.2±0.2 | 100 | ＞ 90 | ≤ 30 |
Made by impregnating PTFE yarn with dimethyl silicone oil.
Made from PTFE raw material with colloidal graphite and lubricating grease added through mixing, drawing,…
Made from PTFE raw material with colloidal graphite and lubricating grease added through mixing, drawing,…
Based on 4105H with aramid fiber added at the center for reinforcement; graphite or other materials can also…
Based on 4105H with high-carbon fiber added at the center for reinforcement; graphite or other materials can…
Fiberglass Fabric with PTFE/TEFLON Coated is made from high performance fiberglass fabric impregnated with…
PTFE Sheet is often chosen for very low friction sideways and wears blocks. PTFE Sheets can provide very low…
PTFE Rod is often chosen to produce bearings because of its very low friction and also for its free running…
PTFE tube is made by plunger extrusion of suspension polymerized PTFE resin. Among all the existing plastics,…